Powder coating additive
  K2065B Matting agent for hybrid□ Incorporated into formula before extrusion □ 1-4.5% by weight of total formula

■Provide 5-70%(60°)of gloss
■Excellent flow and good anti-yellowing
■Wide range of applicability to polyester resins
  K2065F Matting agent for hybrid□ Incorporated into formula before extrusion □ 1-4.5% by weight of total formula

■Provide 8-70%(60°)of gloss
■Excellent flow and fineness surface
■Wide range of applicability to polyester resins
  K2165D Matting agent for hybrid□ Incorporated into formula before extrusion □ 1-5% by weight of total formula

■Provide 8-60%(60°)of gloss
■Good storage stability
■Lower gloss with lower usage
  K2165 Matting agent for hybrid□ Incorporated into formula before extrusion □1-5% by weight of total formula

■Provide 12-70%(60°)of gloss
■Wide range of applicability to polyester resins
■Good flow and anti-yellowing
  K206 Matting agent for PES/TGIC□ Incorporated into formula before extrusion □ 1-3% by weight of total formula

■Provide 30-70%(60°)of gloss
■Good weather resistance and low usage
  K2067A Matting agent for PES/TGIC□ Incorporated into formula before extrusion □ 1-6% by weight of total formula

■Provide 20% (60°)of gloss
■Good flow and excellent anti-yellowing 
■Low wax
  K2061D Matting agent for PES/TGIC□ Dry blend □ 1-1.5% by weight of total formula

■ Provide 10-40% (60°)of gloss
■ Low usage and good gloss stability
  K2167 Matting agent for PES/TGIC□ Incorporated into formula before extrusion □ 2-6% by weight of total formula

■Provide 10%(60°)of gloss
■Good gloss stability and and anti-yellowing
  K2068 Matting hardener for PES/TGIC□ Incorporated into formula before extrusion □ 1-5% by weight of total formula

■Provide 10%(60°)of gloss
■Good flow and good film hardness
  K550 Matting agent (GMA resin) □ Incorporated into formula before extrusion □ Epoxy value is about 700

■The lowest gloss＜5%(60°)
■Excellent weather resistance and anti-yellowing
  K500 Slip and Degassing agent□ Incorporated into formula before extrusion □ 0.5-1% by weight of total formula

■Improve the film appearance and anti-yellowing
■Substitute of benzoin
  K501 Film hardening agent□ Incorporated into formula before extrusion □ 0.5-1% by weight of total formula

■Improve the hardness and smoothness of film
  K5060 Debubbling agent□ Incorporated into formula before extrusion □ or dry blend □ 0.5-1.5% by weight of total formula

■Eliminate pinholes,bubbles and craters 
■Used on porous substrates,such as cast iron,
■cast aluminum alloys
  K5066 Special film hardening agent□ Incorporated into formula before extrusion or dry blend □ 0.5-1.5% by weight of total formula

■Increasing hardness, scratch/friction resistance
  K7318 Low temperature curing accelerator□ Incorporated into formula before extrusion □ 0.3-1% by weight of total formula

■ Reduce curing temperature,shorten curing time
■ Improve leveling and anti-yellowing
■ Reduce the gloss fluctuations with curring temperature
  K7101 Epoxy hardener/curing accelerator□ Incorporated into formula before extrusion □ As curing agent,e the use level is 2-4phr on epoxy resin

■ Excellent flow and low usage
■ Used as curing agent, curing @120℃/30min
■ Used as accelerator, curing @230℃/30s
  K7104 Epoxy hardener□ Incorporated into formula before extrusion □ As sole curative the use level is 3-5phr on epoxy resin

■ Curing @ 140℃/15min or 240℃/30s
■ Applied for thick film coatings or FBE coatings
■ Good mechanical properties
■ Good chemical resistance
  K7108 Epoxy hardener□ Incorporated into formula before extrusion □ As sole curative the use level is 4-6phr on epoxy resin

■ Curing @ 150℃/10min or 240℃/2min
■ Applied for thin film decorative coatings or functional epoxy powder coatings
■ Good film appearance and mechanical strength
  K31 Epoxy hardener/curing accelerator□ Incorporated into formula before extrusion □ As accelerator, use level is 0.1-0.5% on total formula

■For functional or decorative powder coatings
■Curing @ 140℃/30min
  K2830 Epoxy hardener□ Incorporated into formula before extrusion □ 3.5-4.5phr on epoxy resin

■ For functional or decorative powder coatings
■ Curing @ 180℃/15min
  K2831 Epoxy hardener (accelerated DICY)□ Incorporated into formula before extrusion □ 4-5phr on epoxy resin

■For functional or decorative powder coatings 
■Curing @ 160℃/12min or 200℃/5min
  K284 Epoxy hardener (substituted DICY)□ Incorporated into formula before extrusion □ 4-5phr on epoxy resin

■ For high gloss epoxy powder coatings, electric insulative and anti corrosive powder coatings
■ Curing @ 150℃/25min or 180℃/15min
  K3120 β-HAA hardener□ Incorporated into formula before extrusion □ Hydroxyl equivalent value is about 84

■Eco-friendly,Low-toxicity,anti-yellowing
■Exterior application, Substitute of TGIC
  K3120A High purity β-HAA hardener□ Incorporated into formula before extrusion □ Hydroxyl equivalent value is about 84

■A improved product based on K3120
■High purity β-HAA hardener
  K2483 Charge enhancing agent□ Incorporated into formula before extrusion □ 0.3-0.6% by weight of total formula

■Enhance the conductivity
■Improve the film appearance
■Anti yellowing
  K2485 Charge enhancing agent□ Incorporated into formula before extrusion □ 0.2-0.5% by weight of total formula

■Excellent conductivity performance
■Improve the film appearance and flow
■Better overall performance than K2483
  K2486 Charge enhancing agent□ Incorporated into formula before extrusion □ 0.2-0.4% by weight of total formula

■Excellent conductivity performance
■Use for both corona gun and tribo gun
  K300 GMA resin□ Incorporated into formula before extrusion □ Epoxy equivalent value is about 300

■Increase the cross link density
■Improve the mechanical strength and heat  resistance,chemical resistance
  K316 Curing accelerator□ Incorporated into formula before extrusion □0.05-0.5% by weight of total formula

■100% active constituent
■Reduce curing temperature,shorten curing time
  K516 Pigment dispersant□ Incorporated into formula before extrusion □ 0.5-1% by weight of total formula

■Good pigment dispersing ability
■Provide better color strength
■Slightly matting effect
  K003 Anti-yellowing agent□ Incorporated into formula before extrusion □ 0.3-1% by weight of total formula

■Used for all powder coatings,esp.HAA system
■Inhibit yellowing of coatings during the process of both gas baking and electric baking
  K301 Bonding additive□ Refer to the TDS

■ Improve the metal effect of coatings
■ Increase bonding temperature and anti caking
■ Reduce the dosage of metal pigments
  K5501 Stabilizer for metal pigment□ Dry blend □ 2-3% by weight of total formula

■Inhibiting from blackening, spot-formation and loss of brilliance of metallic coatings
■Improve heat resistance
  K5502 Dry powder flow additive□ Dry blend □ 0.1-0.5% by weight of total formula

■ Improving fluidity of coating powders
■ Anti caking
■ Enhancing electrostatic spray efficiency
■ Controlling film thickness for thin coating
  K5503 Adhesion enhancing agent□ Incorporated into formula before extrusion □ 1-3% by weight of total formula

■Improve the wettability and transfer-efficiency  of various kinds of coating powders to substrate
  K7920 Special adhesion enhancing agent□ Incorporated into formula before extrusion □ 0.8-1.5% by weight of total formula

■ Improve the wettability and transfer-efficiency
■ Better to be used on stainless steel substrates and galvanized substrates
  K207 Texture additive□ Incorporated into formula before extrusion □ 0.08-0.15% by weight of total formula

■Impart sand grain finishes
■Use for electrical appliances and IT equipments
  K208 Special texture additive□ Incorporated into formula before extrusion □ 3.5-5% by weight of resin

■For almost all kinds of powder coatings
■Impart special texture finishes such as wrinkle, reticulated, vein, embossed and grained